Structural and optical properties of Ge nanocrystals obtained by hot ion implantation into SiO2 and further ion irradiation

In this work, SiO₂ layers containing Ge nanocrystals (NCs) obtained by the hot implantation approach were submitted to an ion irradiation process with different 2 MeV Si⁺ ion fluences. We have investigated the photoluminescence (PL) behavior and structural properties of the irradiated samples as well as the features of the PL and structural recovery after an additional thermal treatment. We have shown that even with the highest ion bombardment fluence employed (2×10¹⁵ Si/cm²) there is a residual PL emission (12% from the original) and survival of some Ge NCs is still observed by transmission electron microscopy analysis. Even though the final PL and mean diameter of the nanoparticles under ion irradiation are independent of the implantation temperature or annealing time, the PL and structural recovery of the ion-bombarded samples have a memory effect. We have also observed that the lower the ion bombardment fluence, the less efficient is the PL recovery. We have explained such behavior based on current literature data.