Synthesis and photoluminescence properties of YVO4:Eu3+, Al3+ phosphor

The Y_0.95?xAl_xVO₄:5%Eu³⁺ (0≤x≤0.1) phosphors were successfully synthesized by solid state reaction at 900 °C for 6 h, and their luminescence properties were investigated under UV and VUV excitation. Monitoring at 619 nm, a strong broad absorption was enhanced by co-doping of Al³⁺ into the YVO₄:Eu³⁺ lattices at 256 nm under UV excitation. The VUV excitation spectra also showed the enhanced excitation bands at about 156 and 200 nm. Under 254 or 147 nm excitation, it was found that Y_0.95?xAl_xVO₄:Eu³⁺(0≤x≤0.1) phosphors showed strong red emission at about 619 nm corresponding to the electric dipole ⁵D₀^–7F₂ transition of Eu³⁺. The improvement of luminescence intensity of YVO₄:Eu³⁺ was also observed after partial substituting Y³⁺ by Al³⁺ and the optimal luminescence intensity appeared with incorporation of 2.5 mol% Al³⁺.