The interaction of CO and O2 with the (111) surface of Pt3Ti

The electronic properties of clean and partly oxidized Pt₃Ti(111) surfaces have been studied utilizing carbon monoxide both as a probe and as a reducing agent. Vibrational frequencies and desorption profiles of chemisorbed CO as well as ion scattering and angular resolved X-ray photoelectron spectroscopy (XPS) suggest that the first atomic layer of annealed Pt₃Ti(111) is quasi-pure platinum. Scarcely any (θ ≈ 0.01) dissociation of CO was observed. Minor shifts of vibrational frequencies and desorption temperatures compared to Pt(111) and a p(2 × 2) “reconstruction” of the clean surface reveal some influence of the bulk. Auger spectroscopy, XPS, and ion scattering all show an increased titanium signal as a result of oxidation. Surface bound atomic oxygen gives a vibrational band around 650 cm⁻¹ which coincides with infrared absorption spectra of TiO₂. Flashing with CO shifts the band to 500 cm⁻¹. Correlated with this shift we observe (i) CO₂ desorption at a temperature well above that observed for Pt(111)/O, (ii) an altered Ti XPS signal, and (iii) a reduced oxygen concentration. Subsequently adsorbed CO molecules vibrate at the same frequencies as on the bare surface, give the same c(4 × 2) LEED pattern, and desorb at the same temperatures but with reduced intensity, in all proving that the surface oxide only acts as a site-blocker with respect to the metal surface. Our current understanding of these observations is that oxygen creates “islands of TiO₂”, segregated to the surface but with no electronic influence on remaining areas of the platinum enriched metal surface. The hexacoordinated Ti⁴⁺ ions on the surface of these islands are reduced by CO to pentacoordinated Ti³⁺ species. The vibrational shift, 650 to 500 cm⁻¹, can be understood by the dipole active bands of a triatomic O−Ti⁴⁺ −O vibrator compared to a diatomic Ti³⁺−O vibrator.