Migration of Cu ions in Cu2O---Al2O3---SiO2 glasses on heating in air

The behavior of copper ions in the Cu₂O·Al₂O₃·4SiO₂ (in moles) glass on heating in air at temperatures up to 500°C was studied. When the glass, in which about 90% of Cu was present as Cu⁺ ions, was heated in air above 300°C, a CuO layer was formed on the surface. The amount of CuO was increased with heating temperature and time, corresponding to the decrease in weight of the glass. Furthermore, the fraction of Cu²⁺ ions in the glass increased. These observations suggest that oxygens do not diffuse into the glass, but Cu⁺ ions migrate to the surface from the interior to balance the surplus positive charge produced by the oxidation of Cu⁺ to Cu²⁺ ions inside the glass. The following reaction scheme for the formation of the CuO layer was proposed; 2Cu⁺(interior) + ₂¹O₂(surface) → Cu²⁺(interior) + CuO(surface).