Effect of frit size on sintering, crystallization and electrical properties of wollastonite glass-ceramics

Wollastonite glass-ceramics were prepared through pressureless sintering. The sinterability of the prepared samples of the glassy powder in the system (SiO₂-CaO-Na₂O-Fe₂O₃-WO₃) was investigated in the temperature range 720-900 °C and soaking time of 180 min. The influence of the increase in the glass powder particle size on the sinterability and dielectric properties of the glass-ceramic samples was studied.The sintered specimens were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD) methods. XRD analysis revealed that wollastonite was the main crystalline phase in the sintered glass-ceramics. Dielectric properties such as dielectric constant and dielectric loss were measured via a network analyzer at 10 GHz.It was observed that the increase of the glassy powder particle size improved the sinterability and dielectric properties of the glass-ceramic specimens. Wollastonite glass-ceramics with 16 μm particle size had maximum constant and minimum loss (ε_r = 10.10 and tan δ = 0.005) compared with the other glass-ceramics.