Thermal stability of polystyrene blends with polybutadiene,and effects of miscibility of the two polymers on thermal parameter values

The influence of a 1–20% content of polybutadiene (PB) in polystyrene (PS) films on their thermal stability was investigated. It was found that the thermal stabilities of these blends are higher than that of pure PS. This stabilizing effect is significant when the PB content in the blends is 1%. A higher amount of PB causes either no significant change in the thermal stability of the blends (determined in nitrogen) or a rise in thermal stability (determined in air). The cause of these changes is the crosslinking and oxidation which occur with varying efficiency, depending upon the miscibility of the two polymers.

---

Zusammenfassung Es wurde dir thermische Stabilität von Polystyrolfilmen mit einem Polybutadiengehalt von 1–20% untersucht. Es konnte festgestellt werden, daß die thermische Stabilität dieser Mischungen höher liegt als die von reinem Polystyrol. Ein ausgeprägter Einfluß läßt sich bei einem Polybutadiengehalt der Gemische von 1% erkennen. Ein höherer Polybutadiengehalt führt entweder zu keiner weiteren nennenswerten Veränderung der thermischen Stabilität (in Stickstoff) oder zu einer höheren thermischen Stabilität (in Luft) der Gemische. Der Grund für diese Veränderungen liegt in Abhängigkeit von der Mischbarkeit beider Polymere in einer unterschiedlich starken Vernetzung bzw. Oxydation.