| Abstract: | An understanding of the physical and chemical processes involved in the melt polymerization of polyesters in the higher inherent viscosity ranges is of fundamental importance in polyester preparation. For example, the volatile condensation product must diffuse to a polymer–vapor interface before polymerization can take place. Thus, the rate of polymerization of a polyester may be dependent not only upon the chemical kinetics of the polymerization reaction but also upon the diffusion of the condensation product through the polymer melt. The objective of the work presented in this paper was to determine to what degree diffusion or reaction kinetics, or both, limit the melt polycondensation of poly(ethylene terephthalate). Degrees of polymerization in melts between 0.0285 and 0.228 cm in depth at 270°C were measured for various reaction times and were compared with the predictions of mathematical models. The polycondensation rates under these conditions depend upon both the polycondensation rate constant k1 and the diffusivity D of ethylene glycol through the melt. Estimates of the values to these parameters are: k1 = 0.0500 (moles/mole of repeat unit)?1 sec?1; D = 1.66 × 10?4 cm2/sec. |