Characterization of silica-pillared derivatives from aluminum-containing kanemite |
| |
Authors: | Toriya Sunao Takei Takashi Fuji Masayoshi Chikazawa Masatoshi |
| |
Institution: | Department of Applied Chemistry, Graduate School of Engineering, Tokyo Metropolitan University, 1-1 Minami-ohsawa, Hachioji, Tokyo 192-0397, Japan. s-toriya@pop02.odn.ne.jp |
| |
Abstract: | A series of aluminum-containing kanemite (Al-kanemite) samples with several Si/Al molar ratios were synthesized. The Al-kanemite samples were pillared with silica. X-ray diffractograms showed that the layered structure of the Al-kanemite samples was maintained at Si/Al= infinity approximately 10 but was broken at Si/Al = 5, 2.5, and 1. 29Si MAS NMR spectra of the Al-kanemite samples, except for that of Si/Al = 1, mainly showed peaks of Q(3) sites, which were attributed to Si(OSi)(3)(OH) groups, although peaks assigned to Si(OAl)(OSi)(2)(OH) were also seen. The 27Al MAS NMR spectra indicated that the Al-kanemite samples had only four-coordinate aluminum atoms. The FTIR spectra of pyridine adsorbed on the pillared Al-kanemite derivatives revealed Lewis acid sites on the surface. The nitrogen adsorption isotherms of the derivatives were classified as type I (Langmuir) absorption isotherms. Using the alpha(s) method, the specific surface areas of the derivatives were 572-756 m(2)g(-1), and the pore sizes were calculated as 1.25-1.83 nm. The pillared Al-kanemite derivatives had slit-shaped micropore structures. |
| |
Keywords: | |
本文献已被 PubMed 等数据库收录! |
|