| Abstract: | Time-resolved light scattering was employed to investigate kinetics of phase separation in mixtures of poly (ethylene glycol monomethylether) (PEGE)/poly (propylene glycol) (PPG) oligomers. Phase diagrams for PEGE/PPG of varying molecular weights were established by means of cold point measurements. The oligomer mixtures reveal an upper critical solution temperature (UCST). Several temperature quench experiments were carried out with a 60/40 PEGE/PPG blend by rapidly quenching from a single phase (69°C) to two-phase temperatures (66–61°C) at 1°C intervals. As is typical for oligomer mixtures, the early stage of spinodal decomposition (SD) was not detected. The kinetics of phase decomposition was found to be dominated by the late stage of SD. Time-evolution of scattering intensity was analyzed in accordance with nonlinear and dynamical scaling theories. The time dependence of the peak intensity Im and the corresponding peak wavenumber qm was found to follow the power-law {Im(t)? tα, qm(t)? t-β} with the values of α = 3 ± 0.3 and β = 1 ± 0.2, which are very close to the values predicted by Siggia. This process has been attributed to a coarsening mechanism driven by surface tension. In the temporal scaling analysis, the structure function reveals university with time, suggesting self-similarity. Phase separation dynamics in 60/40 PEGE/PPG resembles the behavior predicted for off-critical mixtures. |