| 静压下(CdTe)_2(ZnTe)_4-ZnTe多量子阱结构的多声子共振拉曼散射 |
| |
| 引用本文： | 李国华,刘振先,韩和相,汪兆平,李杰,何力,袁涛金. 静压下(CdTe)_2(ZnTe)_4-ZnTe多量子阱结构的多声子共振拉曼散射[J]. 光散射学报, 1992, 0(1) |
| |
| 作者姓名： | 李国华 刘振先 韩和相 汪兆平 李杰 何力 袁涛金 |
| |
| 作者单位： | 半导体超晶格国家重点实验室中国科学院半导体研究所，半导体超晶格国家重点实验室中国科学院半导体研究所，半导体超晶格国家重点实验室中国科学院半导体研究所，半导体超晶格国家重点实验室中国科学院半导体研究所，中国科学院上海技术物理所，中国科学院上海技术物理所，中国科学院上海技术物理所 北京 100083，北京 100083，北京 100083，北京 100083，上海 200433，上海 200433，上海 200433 |
| |
| 摘 要： | 用加静高压的方法改变光学能隙来实现共振条件。在以(CdTe)_2(ZnTe)_4短周期超晶格为阱层,(ZnTe)_(4)为垒层的多量子阱结构中观察到高达四阶的类 ZnTe 纵光学声子模的多声子共振拉曼散射。通过对拉曼位移随压力变化的分析,发现在与(CdTe)_2(ZnTe)_4短周期超晶格共振时测得的类ZnTe 纵光学声子模的频率比与 ZnTe 势垒层共振时测得的 ZnTe 纵光学声子模的频率低4cm~(-1)。并将它归结为在短周期超品格中纵光学声子模的限制效应。在与短周期超品格严格的2LO 声子出射共振条件下观察到了类 CdTe 的2LO 声子的共振拉曼峰。
|
| 关 键 词： | 共振拉曼散射 量子阱结构 |
Multiphonon resonant Raman scattering from (CdTe)_2(ZnTn)-ZnTe multiple quantum well structure under hydrostatic pressure |
| |
| Li Guohua Liu Zhenxian Han Hexiang Wang Zhaoping. Multiphonon resonant Raman scattering from (CdTe)_2(ZnTn)-ZnTe multiple quantum well structure under hydrostatic pressure[J]. Chinese Journal of Light Scattering, 1992, 0(1) |
| |
| Authors: | Li Guohua Liu Zhenxian Han Hexiang Wang Zhaoping |
| |
| Abstract: | The multiphonon resonant Raman scattering from(CdTe)_2(ZnTe)_4 -ZnTe multiple quantum well structure has been carried out by using the pressure tuning of the optical gap of samples out by using the pressure consists of a(CdTe)_2(ZnTe)_4×8 short period superlattice as the well and a thick ZnTe layer as the barrier.Up to forthorder multiphonon scattering of the ZnTe-like LO phonon modes was observed.It was found that the Raman shift of the ZnTe-like LO phonon modes in resonance with(CdTe)_2(ZnTe)_4 short period superlattices is 4 cm~(-1) lower than that in resonance with ZnTe barrier due to the confined effect of LO phonons in the short period superlattices, The resonant 2LO peak of the CdTe-like modes was aslo observed at the strict out-going resonant condition with the short period superlattices. |
| |
| Keywords: | Resonant Raman scattering Quantum well structure |