The fabrication and performance of an Ag/AgCl reference electrode in human serum

A simple set of electric circuits was used to assemble a pulse generator. With pulse potentials and under galvanostatical control, a clean silver wire was anodized electrochemically for 0.2–0.5 min in 1.0 mol l^?1 HCl with a pulse current density of 20 mA cm^?2, and the pulse wave parameters of t_a/t_c = 1 and a cycle of 4 s forming an Ag/AgCl reference electrode. Even though the AgCl layer was consumed during the working period when the Ag/AgCl electrode was used as a cathode, the AgCl layer could be in situ recovered electrochemically in serum used when a reversed potential was applied to the electrode system immediately after the measuring program was finished. The current response curve of the anode indicated that an AgCl layer in high density was basically accomplished during the first 6 pulse cycles in human serum. In order to keep a stable and uniform AgCl layer on the reference electrode after each measuring cycle, the ratio of the recovery time (t_r) to the working time (t_w) was measured and the smallest value was obtained at 0.03. The open-circuit potential of the Ag/AgCl electrode with respect to a SCE in 0.1 mol l^?1 KCl was monitored over a period of 14 days and the mean value was 40.09 mV vs SCE with a standard deviation of 2.55 mV. The potential of the Ag/AgCl reference electrode did remain constant when the measurements were repeated more than 600 times in undiluted human serum with a standard deviation of 1.89 mV. This study indicated that the Ag/AgCl reference electrode could been rapidly fabricated with a pulse potential and could be used as a reference electrode with long-term stable properties in human serum samples.