| MgCl_2-KCl-AlF_3-(La_2O_3)熔盐体系电解制备Al-Mg-La中间合金 |
| |
| 引用本文： | 张福男,王兆文.MgCl_2-KCl-AlF_3-(La_2O_3)熔盐体系电解制备Al-Mg-La中间合金[J].东北大学学报(自然科学版),2016,37(7):964-968. |
| |
| 作者姓名： | 张福男 王兆文 |
| |
| 作者单位： | (1. 东北大学 冶金学院， 辽宁 沈阳110819； 2. 金策工业综合大学， 朝鲜 平壤999093) |
| |
| 基金项目： | 国家自然科学基金资助项目(51074053). |
| |
| 摘 要： | 在质量比为41.5∶48.5∶10的MgCl_2-KCl-AlF3熔盐体系中加入质量分数为0.6%La_2O_3,利用电解法制备了Al-Mg-La合金.用ICP-OES(电感耦合等离子体光谱仪)和XRD进行了合金的组成和物相分析.研究结果表明,在电解温度800℃,阴极电流密度6.92A/cm2,槽电压5.3~5.4V,电解时间为1h的条件下,电流效率为86.2%,得到的合金主相为α-Mg基体、β-Al12Mg17相与Al11La3相.高的阴极电流密度有利于合金中镁含量的增加.
|
| 关 键 词： | 稀土La Al-Mg-La中间合金 MgCl2-KCl系 MgCl2-KCl-AlF3-La2O3熔盐体系 Al12Mg17相 |
Electrolytic Preparation of Al-Mg-La Master Alloys from MgCl2-KCl- AlF3-(La2O3) Molten Salt |
| |
| JANG Pok-nam,WANG Zhao-wen.Electrolytic Preparation of Al-Mg-La Master Alloys from MgCl2-KCl- AlF3-(La2O3) Molten Salt[J].Journal of Northeastern University(Natural Science),2016,37(7):964-968. |
| |
| Authors: | JANG Pok-nam WANG Zhao-wen |
| |
| Institution: | 1. School of Metallurgy， Northeastern University， Shenyang 110819， China; 2. Kim Chaek University of Technology， Pyongyang 999093， DPR of Korea. |
| |
| Abstract: | 0.6 wt% of La2O3 was dissolved in MgCl2-KCl-AlF3 molten salt system (with mass ratio of 41.5∶48.5∶10). Al-Mg-La master alloy was prepared by electrolysis process. Inductively coupled plasma-optical emission spectroscopy (ICP-OES) and X-ray diffraction (XRD) analysis were used to determine the composition and phases of the alloy. The results show that，the current efficiency can reach 86.2%， and the main alloy phases are α-Mg， β- Al12Mg17 and Al11La3 under the electrolysis conditions of 800℃ of electrolytic temperature， 6.92A/cm2 of cathode current density， 5.3~5.4V of the cell voltage， and 1 hour of electrolysis time. High cathode current density is helpful to increase the magnesium content in the alloy. |
| |
| Keywords: | rare-earth La Al-Mg-La master alloy MgCl2-KCl system MgCl2-KCl-AlF3-La2O3 molten salt Al12 Mg17 phase |