Structure and high-temperature thermoelectric properties of SrAl2Si2

Single crystals of SrAl₂Si₂ were synthesized by reaction of the elements in an aluminum flux at 1000 °C. SrAl₂Si₂ is isostructural to CaAl₂Si₂ and crystallizes in the hexagonal space group P-3m1 (90 K, a=4.1834 (2), c=7.4104 (2) Å, Z=1, R1=0.0156, wR2=0.0308). Thermal analysis shows that the compound melts at ∼1020 °C. Low-temperature resistivity on single crystals along the c-axis shows metallic behavior with room temperature resistivity value of ∼7.5 mΩ cm. High-temperature Seebeck, resistivity, and thermal conductivity measurements were made on hot-pressed pellets. The Seebeck coefficient shows negative values in entire temperature range decreasing from ∼−78 μV K⁻¹ at room temperature to −34 μV K⁻¹ at 1173 K. Seebeck coefficients are negative indicating n-type behavior; however, the temperature dependence is consistent with contribution from minority p-type carriers as well. The lattice contribution to the thermal conductivity is higher than for clathrate structures containing Al and Si, approximately 50 mW cm⁻¹ K, and contributes to the overall low zT for this compound.