Enhanced quantum yield of yellow photoluminescence of Dy ions in nonlinear optical Ba2TiSi2O8 nanocrystals formed in glass

Transparent crystallized glasses consisting of nonlinear optical Ba₂TiSi₂O₈ nanocrystals (diameter: ∼100 nm) are prepared through the crystallization of 40BaO-20TiO₂-40SiO₂-0.5Dy₂O₃ glass (in the molar ratio), and photoluminescence quantum yields of Dy³⁺ ions in the visible region are evaluated directly by using a photoluminescence spectrometer with an integrating sphere. The incorporation of Dy³⁺ ions into Ba₂TiSi₂O₈ nanocrystals is confirmed from the X-ray diffraction analyses. The total quantum yields of the emissions at the bands of ⁴F_9/2→⁶H_15/2 (blue: 484 nm), ⁴F_9/2→⁶H_13/2 (yellow: 575 nm), and ⁴F_9/2→⁶H_11/2 (red: 669 nm) in the crystallized glasses are ∼15%, being about four times larger compared with the precursor glass. It is found that the intensity of yellow (575 nm) emissions and the branching ratio of the yellow (575 nm)/blue (484 nm) intensity ratio increase largely due to the crystallization. It is suggested from Judd-Ofelt analyses that the site symmetry of Dy³⁺ ions in the crystallized glasses is largely distorted, giving a large increase in the yellow emissions. It is proposed that Dy³⁺ ions substitute Ba²⁺ sites in Ba₂TiSi₂O₈ nanocrystals.