Low temperature dielectric dispersion and electrical conductivity studies on Fe2O3 mixed lithium yttrium silicate glasses

Lithium yttrium silicate glasses mixed with different concentrations of Fe₂O₃ of the composition (40 ? x) Li₂O–10Y₂O₃–50SiO₂: x Fe₂O₃, with x = 0.3, 0.5, 0.8, 1.0, 1.2 and 1.5 (all in mol%) were synthesized. Electrical and dielectric properties including dielectric constant, ε′(ω), loss, tan δ, ac conductivity, σ_ac, impedance spectra as well as electric moduli, M(ω), over a wide continuous frequency range of 40 Hz to 10⁶ Hz and in the low temperature range 100 to 360 K were measured as a function of the concentration of Fe₂O₃. The dc conductivity is also evaluated in the temperature range 100 … 360 K. The temperature and frequency dispersions of dielectric constant as well as dielectric loss have been analyzed using space charge polarization model. The ac and dc conductivities have exhibited increasing trend with increasing Fe₂O₃ content beyond 0.5 mol%, whereas the activation energy for the conductivity demonstrated decreasing tendency in this dopant concentration range. Both quantum mechanical tunneling (QMT) and correlated barrier hopping models (CBH) were used for clarification of ac conductivity origin and the corresponding analysis has indicated that CBH model is more appropriate for this glass system. For the better understanding of relaxation dynamics of the electrical properties we have drawn the scaling plots for ac conductivity and also electric moduli. The plots indicated that the relaxation dynamics is independent on temperature but depends on concentration of Fe₂O₃. The dc conductivity is analyzed using small polaron hoping model. The increase of conductivity with the concentration of Fe₂O₃ beyond 0.5 mol% is explained in terms of variations in the redox ratio of iron ions in the glass network. The results were further analyzed quantitatively with the support of experimental data from IR, optical absorption and ESR spectral studies. The overall analysis has indicated that Li₂O–Y₂O₃–SiO₂ glasses containing more than 0.5 mol% of Fe₂O₃ are more suitable for achieving good electrical conductivity in these glasses.