Mixed transition-ion effect in the glass system: Fe2O3-MnO-TeO2

In earlier studies on phosphate and tellurite glasses containing vanadium and iron oxides, non-linear variation of physical properties as functions of the ratios of the transition ions (V/V + Fe) were observed. The most striking effect was observed with electrical conductivity, where a 3 orders of magnitude reduction in conductivity was observed at a V/V + Fe ratio of ~ 0.4. The effect was termed Mixed Transition-ion Effect or MTE. In phosphate glasses, however, MTE was not observed when one of the transition ions was manganese. It was concluded that Mn does not contribute to conduction in these glasses. In the present study, we demonstrate a mixed transition ion effect in tellurite glasses containing MnO and Fe₂O₃ (xFe₂O₃(0.2 ? x) MnO0.8TeO₂ with x varying from 0 to 0.2). A maximum in the property at an intermediate composition (x = 8.5 mol%), was observed in DC resistivity, activation energy, molar volume etc. Mossbauer and optical absorption (UV–VIS–NIR) measurements were performed on these glasses and the transport mechanism has been identified to be hopping of small polarons between Fe^3 + (Mn^3 +) and Fe^2 + (Mn^2 +) sites.