Phase relations in NaxCrxTi8−xO16 at 1350 °C and crystal structure of hollandite-like Na2Cr2Ti6O16

Phase relations of rutile, freudenbergite, and hollandite structures were examined in the pseudobinary system NaCrO₂-TiO₂ (i.e., Na_xCr_xTi_8−xO₁₆) at 1350 °C. The hollandite structure was obtained in the composition range 1.7?x?2.0. The symmetry of the samples at room temperature was tetragonal for x=1.7 and 1.75, and monoclinic for x=1.8 and above. Single crystals of monoclinic hollandite Na₂Cr₂Ti₆O₁₆ were grown and the structure refinement has been carried out using an X-ray diffraction technique. The space group was I2/m and cell parameters were a=10.2385(11), b=2.9559(9), c=9.9097(11)Å, and β=90.545(9)° with Z=1. The Na ion distribution in the tunnel was markedly deformed from that in the tetragonal form. It was suggested that Cr/Ti ratios were different between the two framework metal sites.