Fabrication and optical properties of core-shell structured spherical SiO2@GdVO4:Eu phosphors via sol-gel process

Europium-doped nanocrystalline GdVO₄ phosphor layers were coated on the surface of preformed submicron silica spheres by sol-gel method. The resulted SiO₂@Gd_0.95Eu_0.05VO₄ core-shell particles were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (FESEM), energy-dispersive X-ray spectra (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra, low voltage cathodoluminescence (CL), time resolved PL spectra and kinetic decays. The XRD results demonstrate that the Gd_0.95Eu_0.05VO₄ layers begin to crystallize on the SiO₂ spheres after annealing at 600 ^°C and the crystallinity increases with raising the annealing temperature. The obtained core-shell phosphors have spherical shape, narrow size distribution (average size ca. 600 nm), non-agglomeration. The thickness of the Gd_0.95Eu_0.05VO₄ shells on the SiO₂ cores could be easily tailored by varying the number of deposition cycles (50 nm for four deposition cycles). PL and CL show that the emissions are dominated by ⁵D₀-⁷F₂ transition of Eu³⁺ (618 nm, red). The PL and CL intensities of Eu³⁺ increase with increasing the annealing temperature and the number of coating cycles. The optimum concentration for Eu³⁺ was determined to be 5 mol% of Gd³⁺ in GdVO₄ host.