The A1−xUNbO6−x/2 compounds (x=0, A=Li, Na, K, Cs and x=0.5, A=Rb, Cs): from layered to tunneled structure

Attempts to prepare alkaline metal uranyl niobates of composition A_1−xUNbO_6−x/2 by high-temperature solid-state reactions of A₂CO₃, U₃O₈ and Nb₂O₅ led to pure compounds for x=0 and A=Li (1), Na (2), K (3), Cs (4) and for x=0.5 and A=Rb (5), Cs (6). Single crystals were grown for 1, 3, 4, 5, 6 and for the mixed Na_0.92Cs_0.08UNbO₆ (7) compound. Crystallographic data: 1, monoclinic, P2₁/c, a=10.3091(11), b=6.4414(10), c=7.5602(5) Å, β=100.65(1), Z=4, R₁=0.054 (wR₂=0.107); 3, 5 and 7 orthorhombic, Pnma, Z=8, with a=10.307(2), 10.272(4) and 10.432(3) Å, b=7.588(1), 7.628(3) and 7.681(2) Å, c=13.403(2), 13.451(5) and 13.853(4) Å, R₁=0.023, 0.046 and 0.036 (wR₂=0.058, 0.0106 and 0.088) for 3, 5 and 7, respectively; 6, orthorhombic, Cmcm, Z=8, and a=13.952(3), b=10.607(2) Å, c=7.748(2) Å, R₁=0.044 (wR₂=0.117).The crystal structure of 1 is characterized by layers of uranophane sheet anion topology parallel to the (100) plane. These layers are formed by the association by edge-sharing of chains of edge-shared UO₇ pentagonal bipyramids and chains of corner-shared NbO₅ square pyramids alternating along the 010] direction. The Li⁺ ions are located between two consecutive layers and hold them together; the Li⁺ ions and two layers constitute a neutral “sandwich” {(UNbO₆)⁻-(Li)₂²⁺-(UNbO₆)⁻}. In this unusual structure, the neutral sandwiches are stacked one above another with no formal chemical bonds between the neutral sandwiches.The homeotypic compounds 3, 5, 6, 7 have open-framework structures built from the association by edge-sharing in two directions of parallel chains of edge-shared UO₇ pentagonal bipyramids and ribbons of two edge-shared NbO₆ octahedra further linked by corners. In 3, 5 and 7, the mono-dimensional large tunnels created in the 001] direction by this arrangement can be considered as the association by rectangular faces of two columns of triangular face-shared trigonal prisms of uranyl oxygens. In 3 and 7, all the trigonal prisms are occupied by the alkaline metal, in 5, they are half-occupied. In 6, the polyhedral arrangement is more symmetric and the tunnels created in the 010] direction are built of face-sharing cubes of uranyl oxygens totally occupied by the Cs atoms. This last compound well illustrates the structure-directing effect of the conterion.