Phase formation, crystal chemistry, and properties in the system Bi2O3-Fe2O3-Nb2O5

Subsolidus phase relations have been determined for the Bi₂O₃-Fe₂O₃-Nb₂O₅ system in air (900-1075 °C). Three new ternary phases were observed—Bi₃Fe_0.5Nb_1.5O₉ with an Aurivillius-type structure, and two phases with approximate stoichiometries Bi₁₇Fe₂Nb₃₁O₁₀₆ and Bi₁₇Fe₃Nb₃₀O₁₀₅ that appear to be structurally related to Bi₈Nb₁₈O₅₇. The fourth ternary phase found in this system is pyrochlore (A₂B₂O₆O′), which forms an extensive solid solution region at Bi-deficient stoichiometries (relative to Bi₂FeNbO₇) suggesting that ≈4-15% of the A-sites are occupied by Fe³⁺. X-ray powder diffraction data confirmed that all Bi-Fe-Nb-O pyrochlores form with positional displacements, as found for analogous pyrochlores with Zn, Mn, or Co instead of Fe. A structural refinement of the pyrochlore 0.4400:0.2700:0.2900 Bi₂O₃:Fe₂O₃:Nb₂O₅ using neutron powder diffraction data is reported with the A cations displaced (0.43 Å) to 96g sites and O′ displaced (0.29 Å) to 32e sites (Bi_1.721Fe_0.190(Fe_0.866Nb_1.134)O₇, Fd3¯m (#227), ). This displacive model is somewhat different from that reported for Bi_1.5Zn_0.92Nb_1.5O_6.92, which exhibits twice the concentration of small B-type cations on the A-sites as the Fe system. Bi-Fe-Nb-O pyrochlores exhibited overall paramagnetic behavior with large negative Curie-Weiss temperature intercepts, slight superparamagnetic effects, and depressed observed moments compared to high-spin, spin-only values. The single-phase pyrochlore with composition Bi_1.657Fe_1.092Nb_1.150O₇ exhibited low-temperature dielectric relaxation similar to that observed for Bi_1.5Zn_0.92Nb_1.5O_6.92; at 1 MHz and 200 K the relative permittivity was 125, and above 350 K conductive effects were observed.