Synthesis and applications of biscyclic phosphorus flame retardants

The influence of structural effects of organo-phosphorus flame retardants (FRs) on their flame retardant action was investigated. A series of spirobisphosphorus compounds including 3,9-dibutyl-3,9-dioxo-2,4,8,10-tetraoxa-3,9-diphosphaspiro-5,5-undecane were prepared using various synthetic methods such as the Arbuzov reaction. The chemical structure of the product was confirmed by ¹H and ³¹P NMR. Thermogravimetric analysis (TGA) results reveal that these cyclic phosphorus compounds show a single step degradation in the range of 250-400 °C and act in the gas phase rather than in the condensed phase. The obtained products were blended with an acrylonitrile-butadiene-styrene copolymer (ABS) or polycarbonate (PC) and their flame retardant behavior was evaluated using a UL-94 vertical test. V-0 ratings are achieved at 15-35 wt% loading of FR for ABS and at a much lesser amount of loading for PC. In both cases, it is apparent that the flame retardancy is strongly dependent on the P content of the flame retardant.