Radiation-induced polymerization of 1,1,2-trichlorobutadiene

The γ-ray-induced polymerization of 1,1,2-trichlorobutadiene, m.p. ?48.5°C., was investigated in the temperature range from +55 to ?196°C. In the liquid state, the following results were obtained: (1) the rate decreases with decrease of temperature (E_a = 8.0 kcal./mole); (2) the dose rate dependences of rate and of molecular weight are 0.49 and ?0.25, respectively; (3) the reaction is inhibited by DPPH; (4) the structure of the polymer is predominantly 1,4 units. It was concluded that the liquid-state polymerization proceeds by a radical mechanism, and the radical yield was found to be 19.7. In the solid state, the following results were obtained: (1) the rate is considerably higher than in the liquid state immediately above the melting point and gradually decreases with decrease of temperature (E_a = 0.34 kcal./mole); (2) the dependence of the rate on dose rate is unity while the molecular weight is independent of the dose rate; (3) the reaction rate is unaffected by DPPH and accelerated by dimethylformamide; (4) the structure of the polymer, 3,4 units, is completely different from that of the polymer obtained in the liquid-state polymerization. The solid-state polymerization is probably of a different nature and is not well elucidated.