| Abstract: | A crystal transition was found in nylon 6 fibers from the γ-phase to α-phase on stretching in the chain direction. The γ-phase fiber prepared by iodine treatment was stretched under constant load and the crystal deformation was observed by an x-ray method. The critical stress for the transition was estimated as 4 × 103 kg./cm.2 at room temperature. For this crystal transition the following conditions must be satisfied: (1) extension of the γ-phase chain to untwist the chain around the amide groups, (2) translational mobility of the chain to change the stacking in the crystallite. At the critical stress, the chain in the crystal is extended to nearly the same length as that of α-phase. The translational movement occurs under stress higher than about 3 × 103 kg./cm.2, and the pseudohexagonal cell is deformed into a monoclinic form. However, the monoclinic crystallites present at a stress lower than the critical value estimated above are unstable and may be brought back to the original form by head treatment at 100°C. No crystal transition occurs at low temperature. |