含树枝状大分子PAMAM的苯乙烯乳液聚合

将树枝状大分子PAMAM (4 5代 )作为种子 ,以苯乙烯为代表性单体进行乳液聚合 .研究结果表明 ,加入树枝状大分子PAMAM时 ,所制得的聚合物乳液粒子平均粒径在 30～ 5 0nm之间 ,小于 10 0nm ,且大小分布均匀 ;所制备的聚合物在 16 70cm- 1 左右处出现酰胺的特征吸收峰 ,在 330 0cm- 1 左右处出现N—H伸缩振动特征峰 ;说明树枝状大分子PAMAM起到种子的作用 ,所制备的聚合物含树枝状大分子PAMAM .

EMULSION POLYMERIZATION OF STYRENE CONTAINING DENDRIMER PAMAM

Dendrimers and dendritic polymers have applications in a diverse range of many fields including medical,electronics,nanotechnolody,biology and catalysis.Dendrimers are known for their well-defined,highly branched architectures that are built in a stepwise manner.Using dendrimer PAMAM (generation 4.5) as seed,the monodisperse and nano-sized polystyrene emulsions containing dendrimer PAMAM have been obtained by seed emulsion polymerization.The size and size distribution of particles were characterized by Transmission Electron Microscopy (TEM) and Dynamic Light Scattering (DLS).It has been found that when PAMAM is used,the diameters of emulsion particles are much smaller than 100 nm,and the particles are nearly monodisperse,which are not easily obtained from other emulsion polymerization systems.The FT-IR spectrums showed obviously that,when PAMAM is used,there are absorption peak at ca.1670 cm~(-1) and stretching peak at ca.3300 cm~(-1) which mean that the dendrimer is included in the obtained polymer.