Swelling effect onα-relaxation in high density polyethylene |
| |
Authors: | Hidekiko Arai Dr Isamu Kuriyama |
| |
Institution: | (1) Japan Atomic Energy Research Institute, Takasaki;(2) Radiation Chemistry Research Establishment Takasaki, Gumna, Japan |
| |
Abstract: | Summary Swelling effects of carbon tetrachloride on the mechanical relaxations in the crystal mat and the melt-crystallized samples of high density polyethylene were studied using a torsion pendulum. A very strong -relaxation peak appears by swelling at the low temperature side of the original -relaxation for the crystal mat. It was shown that this strong -relaxation originates from the slippage between the highly swollen lamellae. For the melt-crystallized sample, the -relaxation peak is decreased by swelling, but its temperature is unchanged. This behavior suggests that the -relaxation in the melt-crystallized sample originates mainly from deformation process of intermosaic block region. The swelling effect on -relaxation was also discussed.
Zusammenfassung Quellungseffekte von Tetrachlorkohlenstoff auf das mechanische Relaxationsverhalten in Einkristall-Matten und schmelzkristallisierten Proben von linearem Polyäthylen wurden mit den Torsionspendeln untersucht. Ein sehr starkes -Maximum tritt durch die Quellung bei tieferen Temperaturen als der der -Relaxation in den nicht gequollenen Einkristall-Matten auf. Es wird gezeigt, daß diese starke -Relaxation auf das Gleiten der ausreichend gequollenen Lamellen zurückzuführen ist. Bei schmelzkristallisierten Proben wird das -Maximum durch die Quellung erniedrigt, seine Temperaturlage wird jedoch nicht verändert. Dies zeigt, daß die -Relaxation in der schmelzkristallisierten Probe hauptsäcblich auf Deformations-Prozessen in den Blöcken beruht. Auch die Quellungseffekte auf die -Relaxationen wurden diskutiert. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|