Effect of styrene–acrylonitrile content on 0.5?M NaI/0.05?M I2 liquid electrolyte encapsulation for dye-sensitized solar cells

The effect of a gel polymer electrolyte (GPE) as the redox electrolyte used in dye-sensitized solar cells was studied. A GPE solution consisting of 0.5?M sodium iodide, 0.05?M iodine, and ethylene carbonate/propylene carbonate (1:1 w/w) binary solvents was mixed with increasing amounts of styrene–acrylonitrile (SAN). Bulk conductivity measurements show a decreasing trend from 4.54 to 0.83×10^?3?S?cm^?1 with increasing SAN content. The GPE exhibits Newtonian-like behavior and its viscosity increases from 0.041 to 1.093?Pa?s with increasing SAN content. A balance between conductivity (1.3?×?10^?3?S?cm^?1) and viscosity (1.4?Pa?s) is observed at 19?wt.% SAN. Fourier transform infrared spectroscopy detects elevated ring torsion at 706?cm^?1 upon the addition of SAN into the liquid electrolyte. This indicates that SAN does not bond with the liquid electrolyte. Finally, the potential stability window of 19?wt.% SAN, which ranges from ?1.68 to 1.38?V, proves its applicability in solar cells.