Glass formation and crystallization behavior in Mg65Cu25Y10−xGdx (x=0, 5 and 10) alloys

The glass forming ability and crystallization behavior of Mg₆₅Cu₂₅Y_10−xGd_x (x=0, 5 and 10) alloys have been investigated. The glass forming ability (GFA) is significantly improved when Y in Mg₆₅Cu₂₅Y₁₀ is substituted with Gd. Ternary Mg₆₅Cu₂₅Gd₁₀ bulk metallic glass (BMG) with diameter of at least 8 mm was successfully fabricated by conventional Cu-mold casting method in air atmosphere. Mg₂(Y, Gd) is the first competing crystalline phase against the glass formation in the Mg₆₅Cu₂₅Y_10−xGd_x (x=0, 5) alloys, while Mg₂Cu and Cu₂Gd are the competing crystalline phases in the Mg₆₅Cu₂₅Gd₁₀ alloy. Therefore, the suppression of the formation of Mg₂(Y, Gd) during cooling from the liquid improves the GFA significantly.