Abstract: | The polymerization of methyl α-ethylacrylate was carried out in toluene by n-BuLi at various temperatures. The yield of the polymer decreased with increase in the polymerization temperature and at 30°C and above no polymer was obtained, indicating that the ceiling temperature of this monomer lay between 0 and 30°C. The isotacticity increased with an increase in the polymerization temperature and at 0°C a highly isotactic polymer was obtained. The fractionation of the polymer obtained at ?78°C showed that the polymer was a mixture of isotactic and syndiotactic ones. Upon the addition of a small amount of methanol or water in the polymerization mixture the isotacticity of the polymer increased while the yield decreased. Syndiotactic polymer was obtained in the polymerization by n-BuLi in tetrahydrofuran as well as by diisobutyl aluminum diphenylamide in toluene. |