Study of the microstructure and mechanical properties of white clam shell |
| |
| Affiliation: | 1. Seafloor Hydrothermal Activity Laboratory of the Key Laboratory of Marine Geology and Environment, Institute of Oceanology, Chinese Academy of Sciences, Qingdao 266071, China;2. Laboratory for Marine Mineral Resources, Qingdao National Laboratory for Marine Science and Technology, Qingdao 266071, China;3. University of Chinese Academy of Sciences, Beijing 100049, China;4. Qingdao Collaborative Innovation Center of Marine Science and Technology, Qingdao 266061, China;5. Marine Biological Museum, Institute of Oceanology, Chinese Academy of Sciences, Qingdao 266071, China;1. Royal Belgian Institute of Natural Sciences, Rue Vautier 29, 1000 Brussels, Belgium;2. Evolutionary Ecology Group, University of Antwerp, Groenenborgerlaan 171, 2020 Antwerp, Belgium;3. Rue Alphonse Renard 29, 1050 Brussels, Belgium |
| |
| Abstract: | The microstructure and mechanical properties of white clam shell were investigated, respectively. It can be divided into horny layer, prismatic layer and nacreous layer. Crossed-lamellar structure was the microstructural characteristic. The extension direction of lamellae in prismatic layer was different from that in nacreous layer, which formed an angle on the interface between prismatic layer and nacreous layer. The phase component of three layers was CaCO3 with crystallization morphology of aragonite, which confirmed the crossed-lamellar structural characteristic. White calm shell exhibited perfect mechanical properties. The microhardness values of three layers were 273 HV, 240 HV and 300 HV, respectively. The average values of flexure and compression strength were 110.2 MPa and 80.1 MPa, respectively. The macroscopical cracks crossed the lamellae and finally terminated within the length range of about 80 μm. It was the microstructure characteristics, the angle on the interface between prismatic and nacreous layer and the hardness diversity among the different layers that enhanced mechanical properties of white calm shell. |
| |
| Keywords: | Shell Microstructure Phase component Mechanical properties |
| 本文献已被 ScienceDirect 等数据库收录！ |
|