TEM-Untersuchungen von Gitterfehlern in ZnSiP2-Einkristallen

Results are dealt with concerning TEM investigations of lattice defects in ZnSiP₂ single crystals. After the crystal growth dislocations or stacking faults were found in a few cases only. More frequently twins were present in the microstructure. The crystallographic elements of twinning are {112} 〈111〉. After plastic deformation by bending at 900 °C local dislocation arrangements with high defect density (N_v ≈ 10⁶…︁ 10⁷ cm⁻²) were observed. By means of the diffraction contrast one Burgers vector b = 1/2 〈111〉 could be identified. In some cases the crystals also contained wide deformation stacking faults, which were limited by partial dislocations. The density of twins was not increased under the conditions of deformation reported here. As it can be concluded from investigations of Oettel et al. and from the results of the twin analysis, slip and generation of stacking faults take place on {112}-planes in ZnSiP₂ crystals. Crystallographic considerations on both processes are dealt with.