Synthesis, structure and properties of new chain cuprates, Na3Cu2O4 and Na8Cu5O10

Na₃Cu₂O₄ and Na₈Cu₅O₁₀ were prepared via the azide/nitrate route from stoichiometric mixtures of the precursors CuO, NaN₃ and NaNO₃. Single crystals have been grown by subsequent annealing of the as prepared powders at 500 °C for 2000 h in silver crucibles, which were sealed in glass ampoules under dried Ar. According to the X-ray analysis of the crystal structures (Na₃Cu₂O₄: P2₁/n, Z=4, a=5.7046(2), b=11.0591(4), c=8.0261(3) Å, β=108.389(1)°, 2516 independent reflections, R₁(all)=0.0813, wR₂ (all)=0.1223; Na₈Cu₅O₁₀: Cm, Z=2, a=8.228(1), b=13.929(2), , β=111.718(2)°, 2949 independent reflections, R₁(all)=0.0349, wR₂ (all)=0.0850), the main feature of both crystal structures are CuO₂ chains built up from planar, edge-sharing CuO₄ squares. From the analysis of the Cu-O bond lengths, the valence states of either +2 or +3 can be unambiguously assigned to each copper atom. In Na₃Cu₂O₄ these ions alternate in the chains, in Na₈Cu₅O₁₀ the periodically repeated part consists of five atoms according to Cu^II-Cu^II-Cu^III-Cu^II-Cu^III. The magnetic susceptibilities show the dominance of antiferromagnetic interactions. At high temperatures the compounds exhibit Curie-Weiss behaviour (Na₃Cu₂O₄: , , Na₈Cu₅O₁₀: , , magnetic moments per divalent copper ion). Antiferromagmetic ordering is observed to occur in these compounds below 13 K (Na₃Cu₂O₄) and 24 K (Na₈Cu₅O₁₀).