Structural models for intergrowth structures in the phase system Al2O3-TiO2

The phase system Al₂O₃-TiO₂ was investigated in the compositional range from 48:52 to 62:38 mol% Al₂O₃:TiO₂. The samples were prepared by melting the binary oxides in an arc-imaging furnace and the obtained samples were examined by powder X-ray diffraction. The recorded powder patterns could be interpreted in terms of intergrowth structures consisting of two basic building blocks, which were deduced from the known crystal structures of β-Al₂TiO₅ and Al₆Ti₂O₁₃. The structure of a new ordered compound with the formula Al₁₆Ti₅O₃₄ is proposed. The thermal stability was estimated from DTA and tempering experiments and showed that all prepared samples decompose at temperatures around 800 °C into the binary oxides corundum and titania.