Investigation on spectral features of tungsten ions in PbO-Bi2O3-As2O3 glass matrix

Lead bismuth arsenate glasses mixed with different concentrations of WO₃ (ranging from 0 to 6.0 mol%) were synthesized. Differential thermal analysis (DTA), optical absorption, ESR and IR spectral studies have been carried out. The results of DTA have indicated that there is a gradual decrease in the resistance of the glass against devitrification with increase in the concentration of WO₃ upto 4.0 mol%.The optical absorption spectra of these glasses exhibited a relatively broad band peaking at about 880 nm identified due to d_xy→d_x²_−y² transition of W⁵⁺ ions; this band is observed to be more intense in the spectrum of glass containing 4.0 mol% of WO₃. Further, two prominent kinks attributed to ³P₀→¹S₀, ¹D₂ transitions of Bi³⁺ ions have also been located in the absorption spectra. The ESR spectra of these glasses recorded at room temperature exhibited an asymmetric signal at g_⊥∼1.71 and g_ll∼1.61. The intensity of the signal is observed to be maximal for the spectrum of the glass W₄. The quantitative analysis of optical absorption and ESR spectral studies have indicated that there is a maximum reduction of tungsten ions from W⁶⁺ state to W⁵⁺ state in the glass containing 4.0 mol% of WO₃. The IR spectral studies have indicated that there is a increasing degree of disorder in the glass network with increase in the concentration of WO₃ upto 4.0 mol%.