Growth of big single crystals of a new magnetic superconducting double perovskite Ba2PrRu1–xCuxO6

Single crystals of Ba₂PrRu_1–xCu_xO₆ with x = 0 to 0.2, have been grown from high temperature solutions of a mixture of PbO‐PbF₂ in the temperature range 1100–1200 °C. Thin crystals with mostly a hexagonal and triangular plate like habit measuring up to 1–2 mm across and 0.1–0.2 mm thick were obtained. The size, quality and morphology of the crystals were improved by varying the solution volume as well as additives like B₂O₃. Large crystals measuring up to 3 mm across and 0.3 to 0.5 mm thick were obtained with 5–7 wt% solute concentration and 0.51 wt% of B₂O₃. The ZFC curves exhibit a spin glass like behavior with x = 0 and a superconducting transition at 8 to 11 K depending on x = 0.05 to 0.1. The transition was also influenced by the growth temperature and post growth annealing. Powder x‐ray diffraction, EDS and Raman spectroscopic measurements confirm the presence of Cu in the crystals. (© 2006 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)