Evaporation induced diameter control in fiber crystal growth by micro‐pulling‐down technique: Bi4Ge3O12

Diameter self‐control was established in Bi₄Ge₃O₁₂ fiber crystal growth by micro‐pulling‐down technique. In accordance with Bi₂O₃‐GeO₂ phase diagram, the diameter was controlled due to compensation of solidification with evaporation of volatile Bi₂O₃ self‐flux charged into the crucible with excess. The crucibles had capillary channels of 310 or 650 μm in outer diameter. The crystals up to 400 mm long and 50‐300 μm in diameter were grown at pulling‐down rates of 0.04‐1.00 mm/min. The melt composition and the pulling rate were generally only two parameters determining solidification rate. As a result, crystals with uniform (± 10%) diameter and aspect ratio up to 10⁴ were produced without automation of the process. (© 2006 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)