Phase equilibria in the pseudo-binary system SrO-Fe2O3

The phase relations in the pseudo-binary system SrO-Fe₂O₃ have been investigated in air up to 1150°C by means of powder X-ray diffraction and thermal analysis. Sr₃Fe₂O_7−δ, SrFeO_3−δ and SrFe₁₂O₁₉ are stable phases in the entire investigated temperature region, whereas Sr₂FeO_4−δ and Sr₄Fe₃O_10−δ decompose above 930±10°C and 850±25°C, respectively. Sr₄Fe₆O_13±δ is entropy-stabilized relative to SrFeO_3−δ and SrFe₁₂O₁₉ above 775±25°C. Extended solid-solution Sr_1±xFeO_3−δ was demonstrated. On the Fe-deficient side, the extent of solid solubility appeared to decrease gradually with temperature, whereas an abrupt decrease due to formation of Sr₄Fe₆O_13±δ was observed above 775°C on the Sr-deficient side.