Solid state phase equilibria in the Gd-Si-B system at 1270 K

Solid state phase equilibria in the ternary Gd-Si-B phase diagram have been proposed at 1270 K using X-ray diffraction, scanning electron microscopy and electron probe microanalysis. Prior to this work, the binary systems Gd-B, Gd-Si and Si-B have also been reinvestigated. The main characteristic of the ternary diagram is the occurrence of two new ternary compounds Gd₅Si₂B₈ and Gd₅Si₃B_0.64. The former crystallizes in tetragonal symmetry, space group P4/mbm with unit cell parameters a=7.2665(3), c=8.2229(7) Å, the second one presents hexagonal symmetry, space group P6₃/mcm with unit cell parameters a=8.5080(4),c=6.4141(2) Å. The X-ray structures of the two structurally related phases Gd₅Si₃B_0.64 and host binary Gd₅Si₃ have been refined from three-dimensional single-crystal intensity data to the final R values of 0.036 (R_w=0.046) and 0.046 (R_w=0.055) for 457 and 401 reflections, respectively with [F>4σ(F)]. Both structures exhibit the Mn₅Si₃-type structure, with in addition for Gd₅Si₃B_0.64 a partial occupancy by boron of the normally vacant interstitial site at the center of the Gd₆ octahedron, which corresponds to the origin of the unit cell. Bonding between the interstitial boron atoms and the gadolinium ones forming the Gd₆B polyhedra is indicated by the decrease in the corresponding Gd-Gd distances and consequently in the unit cell volume. Finally, the Gd-Si-B phase diagram is compared with the previously reported Er-Si-B, at 1070 K.