Lifetime prediction of ABS polymers based on thermoanalytical data

The service life of ABS polymer, stabilized by 2-(3,5-di-tert-butyl-4-hydroxyanilino)-4,6-bis(octylthio)-1,3,5-triazine and containing 50% of a modifying rubber component, was estimated from oxidative induction times measured by DSC in isothermal mode in the temperature interval 140–170°C. The lifetime of ABS powder at the actual temperature of drying was predicted by linear extrapolation according to Arrhenius. However, the extrapolated value was much longer than the real lifetime determined from the long-term oven aging tests at 70 and 90°C, simulating the industrial drying process. The effect of changes in the apparent activation energy of oxidation due to antioxidant consumption during polymer aging is discussed.