| Abstract: | Conclusions 1. The temperature dependences obtained for the ultimate alongation, tensile strength, and elastic modulus of various polymers showed that the relationship between the mechanical properties and chemical structure of macromolecules found in our earlier work at 4.2°K is retained at 78°K and, possibly, up to 90°K.2. It was shown that the passage of the tensile strength through a maximum upon warming from 4.2°K results from a corresponding increase in deformability, which is accompanied by a decrease in the elastic modulus and deviation of the polymer bodies from Hooke's law progressively with increasing temperature.3. It was shown that the amorphization of crystallizing polymers, for example, by quenching, gives a marked change in the deformability, tensile strength, and elasticity of the polymer body over the entire range from 300 down to 4.2°K.4. Study of the mechanical properties of polymers at 78°K in a helium medium and liquid nitrogen showed a marked effect of contact of the polymer with liquid nitrogen on these properties. This effect is different for polymers of varying chemical structure as well as for the same polymer in different physical states.Report presented at the Third All-Union Conference on Polymer Mechanics, Riga, November 10–12, 1976.L. Ya. Karpov Scientific-Research Institute of Physical Chemistry, Moscow. Translated from Mekhanika Polimerov, No. 3, pp. 387–391, May–June, 1977. |