HETEROAROMATIC POLYMERS — HIGH TEMPERATURE POLYPYRROLONES DERIVED FROM 2,6-BIS(3'',4''-DIAMINOPHENYL)-4-BIPHENYLPYRIDINE AND VARIOUS AROMATIC DIANHYDRIDES

A new type of aromatic tetraarnine containing biphenyl moiety in the side chain was synthesized via a modified Chichibabin＇s reaction. 3-Nitro-4-acetamidoacetophenone was reacted with 4-phenyl benzaldehyde in the presence of ammonium acetate to obtain 2,6-bis（3＇,4＇-diaminophenyl）-4-biphenyl pyridine （DPPA）. A series of polypyrrolones （PPys） were prepared using tetraamine and various aromatic dianhydrides via a two-step cyclization procedure. All the PPys show excellent high temperature stabilities with the initial decomposition temperatures of 530-549℃ and residual weight ratio of 49%-80% at 750℃ in nitrogen. The polymers exhibit no apparent glass transition temperatures （Tgs） except PPy-1 （Tg= 327℃）, which is derived from tetraamine DPPA and 2,2-bis[4-（3＇,4＇-dicarboxyphenoxy）-phenyl]propane dianhydride （BPADA）. In addition, the polymers have acceptable mechanical properties with the tensile strength of 65-94 MPa. The PPy films show excellent hydrolysis-resistance in alkaline aqueous medium and could maintain most of the properties even after boiling in 10% aqueous sodium hydroxide solution for a week.

HETEROAROMATIC POLYMERS — HIGH TEMPERATURE POLYPYRROLONES DERIVED FROM 2,6-BIS(3',4'-DIAMINOPHENYL)-4-BIPHENYLPYRIDINE AND VARIOUS AROMATIC DIANHYDRIDES

 A new type of aromatic tetraamine containing biphenyl moiety in the side chain was synthesized via a modified Chichibabin’s reaction. 3-Nitro-4-acetamidoacetophenone was reacted with 4-phenyl benzaldehyde in the presence of ammonium acetate to obtain 2,6-bis(3¢,4¢-diaminophenyl)-4-biphenyl pyridine (DPPA). A series of polypyrrolones (PPys) were prepared using tetraamine and various aromatic dianhydrides via a two-step cyclization procedure. All the PPys show excellent high temperature stabilities with the initial decomposition temperatures of 530-549℃ and residual weight ratio of 49%-80% at 750℃ in nitrogen. The polymers exhibit no apparent glass transition temperatures (Tgs) except PPy-1 (Tg = 327℃), which is derived from tetraamine DPPA and 2,2-bis[4-(3¢,4¢-dicarboxyphenoxy)-phenyl]propane dianhydride (BPADA). In addition, the polymers have acceptable mechanical properties with the tensile strength of 65-94 MPa. The PPy films show excellent hydrolysis-resistance in alkaline aqueous medium and could maintain most of the properties even after boiling in 10% aqueous sodium hydroxide solution for a week.