钛氧纳米管固载Rh催化剂催化氰基烯烃氢甲酰化反应性能

为了调控含碱性基团功能烯烃的催化氢甲酰化反应，设计合成了不同表面酸性的钛氧纳米管和Zr-掺杂钛氧纳米管负载Rh催化剂（Rh/TNTs，Rh/Zr-TNTs）。用XRD、XPS、FT-IR、TEM和低温N2吸脱附等对所合成的催化剂进行了结构及组成表征。催化剂没有显现出与Rh和Zr相关的XRD衍射峰，Rh在纳米管中高度分散；Zr-掺杂钛氧纳米管的比表面积比纯钛氧纳米管的要高，催化剂的比表面积随着载Rh量的增加而减小，其中Rh0百分率也会降低，催化剂中Rh能对CO进行化学吸附。所合成的催化剂能有效地催化氰基烯烃氢甲酰化，催化活性随载Rh量而变化，最佳值为0.13 w；提高催化温度虽能增加2-甲基-3-丁烯腈的转化率，但也有利于它的异构化；Rh/Zr-TNTs表面更强的B酸性有利于催化反应生成直链产物醛，负载催化剂能表现出良好的协同作用。

Ti-O Nanotubes Supported Rh-catalysts and their Catalytic Performances for Hydroformylation Reaction of Olefin Containing -CN Functional Group

To develop an efficient catalyst system for hydroformylation of functionalized olefin, titania and Zr-doped titania nanotubes supported Rh-catalysts were synthesized. The catalysts were characterized with XRD, XPS, FT-IR, TEM and N2 adsorption-desorption. The XRD patterns for catalysts did not show the diffraction peak related to Rh, which should be ascribed to that Rh was highly dispersed on the outer and inner surface of nanotubes. The SSA of Zr-doped titania nanotubes was higher than that of primary one, and with the increase of Rh-loading amount the SSA of catalysts decreased, but the percentage of Rh0 state in the catalysts dropped slightly; the chemisorption of CO on Rh0 showed a clear FT-IR peak at 1802.65cm-1. The catalysts all displayed catalytic activity for the hydroformylation reaction of olefin containing -CN functional group and the activity varied with the Rh-loading amount, the optimal Rh-loading amount was about 0.13 w. Raising reaction temperature was favorable for the conversion of 2M3BN, but high temperature would lead to more isomerization of 2M3BN. The B-acid on Rh/Zr-TNTs was favorable for the formation of linear aldehyde.