Mossbauer, infrared and magnetic susceptibility studies of iron sodium borate glasses doped by sulphur

The affect of sulphur on the structural properties of iron sodium diborate glasses having the composition {(100−x)Na₂B₄O₇+xFe₂O₃}+yS, where x=0.05, 0.15 and 0.25 mol% and Y=0, 2.5 and 5 wt% was studied by infrared, Mossbauer spectroscopy and magnetic susceptibility measurements. It was found that, for samples having 5 mol% Fe₂O₃ and free from sulphur, the iron ions are present in both Fe²⁺ and Fe³⁺ states and also 92% of the total iron enters the glass network as a glass former. The ratio of Fe³⁺/Fe²⁺ increases with increasing the iron content for sulphur-free samples and others containing sulphur. This ratio also decreases with increasing the sulphur content. The magnetic susceptibility was found to decrease with increasing the sulphur content. Also, the increase of Fe₂O₃ content led to a less symmetrical environment of Fe³⁺ ions and vice versa for the Fe²⁺ environment.