Stereocomplex poly(lactic acid) vascular stents by 3D‐printing with long chain branching structures: Toward desirable crystallization properties and mechanical performance

Using pyromelliticdianhydride (PMDA) and polyfunctional epoxy ether (PFE) as branching agent, long chain branching stereocomplex poly(L‐lactide)s and poly(D‐lactide)s was prepared by reactive processing, respectably. Then stereocomplex poly(lactide)s of long chain branching PLLA and PDLA (sc‐PLA/BA) was prepared by solution blending and its fabricated the vascular stents via 3D‐printing.The effects of branching structure on melt crystallization behavior of sc‐PLA/BA investigated by DSC. The influence of the branching agent content on the crystallization ability of samples shows a bell‐shaped relationship, there is a maximum point when the branching agent content is1.5 wt%. When the branching agent content is less than 1.5 wt%, the crystallization ability of the sample increased with the increasing of branching agent content. When the branching agent content exceeded than 1.5 wt%, the crystallization ability of the samples decreased with branching agent content increasing. Such behavior is as the linear PLA branched to dendrite configuration, the enrichment of segments around branching structure within branched chains promoted its nucleation. But the high degree of branching caused inter‐ or intrachians entanglement which obstructed the segments movement and growth into the crystals. The half‐time of crystallization (t_1/2) of the samples decreased from 6 minutes for initial sc‐PLA/BA‐0 to 3 minutes of sc‐PLA/BA‐1.5 wt% at 163°C. POM results indicated that nucleation density of sc‐PLA/BA significantly increased with the branching agent increasing. Moreover, mechanical testing demonstrated that forming branching structure could be an effective modification of the mechanical properties for sc‐PLA, its tensile strength and modulus increases from 57.3 MPa and 2.02 GPa to 70.4 MPa and 3.31 GPa, respectively. TGA results analyzed by FWO method and Kissinger method, indicated the apparent activation energy of sc‐PLA/BA samples increases from 96.8 to 113.3 kJ/mol, suggesting the improvement of heat resistance. The CCK‐8 assay, ALP assay and cell Live/Dead assay results indicated that sc‐PLA with branching structure presented very low cell cytotoxicity. Therefore, the long chain branching sc‐PLA matrix with branching agent could effectively improve its crystallization abilities, mechanical properties, heat resistance and biocompatibilities.