The dynamic growth of a single void in a viscoplastic material under transient hydrostatic loading |
| |
Authors: | XY Wu TW Wright |
| |
Institution: | a Department of Mechanical Engineering, The Johns Hopkins University, Baltimore, MD 21218, USA b U.S. Army Research Laboratory, Aberdeen Proving Ground, MD 21005, USA |
| |
Abstract: | We have examined the problem of the dynamic growth of a single spherical void in an elastic-viscoplastic medium, with a view towards addressing a number of problems that arise during the dynamic failure of metals. Particular attention is paid to inertial, thermal and rate-dependent effects, which have not previously been thoroughly studied in a combined setting. It is shown that the critical stress for unstable growth of the void in the quasistatic case is strongly affected by the thermal softening of the material (in adiabatic calculations). Thermal softening has the effect of lowering the critical stress, and has a stronger influence at high strain hardening exponents. It is shown that the thermally diffusive case for quasistatic void growth in rate-dependent materials is strongly affected by the initial void size, because of the length scale introduced by the thermal diffusion. The effects of inertia are quantified, and it is demonstrated that inertial effects are small in the early stages of void growth and are strongly dependent on the initial size of the void and the rate of loading. Under supercritical loading for the inertial problem, voids of all sizes achieve a constant absolute void growth rate in the long term. Inertia first impedes, but finally promotes dynamic void growth under a subcritical loading. For dynamic void growth, the effect of rate-hardening is to reduce the rate of void growth in comparison to the rate-independent case, and to reduce the final relative void growth achieved. |
| |
Keywords: | A Dynamic fracture Dynamics Voids and inclusions Shock waves B Viscoplastic materials |
本文献已被 ScienceDirect 等数据库收录! |
|