Synthesis and characterization of UV‐curable ladder‐like polysilsesquioxane |
| |
| Authors: | Seung–Sock Choi Albert S Lee He Seung Lee Hyeon Yeol Jeon Kyung–Youl Baek Dong Hoon Choi Seung Sang Hwang |
| |
| Institution: | 1. Nano Hybrids Research Center, Korea Institute of Science Technology, Seongbuk‐gu, Seoul 136‐791, Korea;2. Department of Chemistry, Korea University, Seongbuk‐gu, Seoul 136‐701, Korea |
| |
| Abstract: | Various ladder‐like structured poly(phenyl‐co‐methacryl silsesquioxane)s (LPMSQ)s with high molecular weight (Mw = 10,000 ～ 40,000) were synthesized by direct hydrolysis and polymerization in the presence of base catalyst at 25 °C. Synthesized LPMSQs mainly showed ladder‐like structure and photo‐cure reaction by 100 mW/cm2 (360 nm) for 10 s without any photo‐cure initiators. Chemical composition and structural analysis of the obtained LPMSQs were characterized using 1H NMR, 29Si NMR, Fourier transform infrared spectroscopy (FTIR), gel permeation chromatography (GPC), and X‐ray diffraction (XRD). Physical properties of LPMSQs before and after photcuring were analyzed by Nanoindentation. Surface modulus increased to 8GPa and hardness of thin films increased from 100 to 400 MPa. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011 |
| |
| Keywords: | materials science organic‐inorganic hybrid composite organic‐inorganic hybrid material photochemistry silsesquioxane UV‐curable material |
|
|