Preparation, phase transformation and microstructure of ZrxTi1−xO2 (x = 0.1-0.9) fine fibers

Zr_xTi_1−xO₂ (x = 0.1-0.9) fibers were prepared by the sol-gel dry-spinning method. Polyacetylacetonatozirconium (PAZ) and tetrabutyl titanate (C₁₆H₃₆O₄Ti) were used as raw materials. The green fibers were obtained from the amorphous spinnable solution and then heat-treated to convert into polycrystalline fibers. The main phase changes from TiO₂ to zirconium titanate (ZT) and then tetragonal ZrO₂ with increasing ZrO₂ content. The crystallization temperature varied with the molar ratio of Zr:Ti. The heat-treated fibers at 1050 °C have few pores and no cracks with diameters of 10-20μm and lengths of 1-5 cm.