Thermal diffusivity measurements on As-Te-Ga glasses by photo-thermal deflection technique: Composition dependence and topological thresholds |
| |
Authors: | N. Manikandan |
| |
Affiliation: | Department of Instrumentation, Indian Institute of Science, Bangalore 560 012, India |
| |
Abstract: | The thermal diffusivity (α) of As20Te80−xGax glasses (7.5 ? x ? 18.5) has been measured using photo-thermal deflection (PTD) technique. It is found that the thermal diffusivity is comparatively lower for As20Te80−xGax glasses, which is consistent with the memory type of electrical switching exhibited by these samples. Further, the thermal diffusivity of As20Te80−xGax glasses is found to increase with the incorporation of gallium initially (for x ? 9), which is consistent with the metallicity of the additive. This increase in α results in a maximum at the composition x = 9; beyond x = 9, a decrease is seen in α leading to a minimum at the composition x = 15. The observed composition dependence of thermal diffusivity of As20Te80−xGax glasses has been found to be similar to that of Al20AsxTe100−x glasses, based on which it is proposed that As20Te80−xGax glasses exhibit an extended stiffness transition with compositions x = 9 and x = 15 being its onset and completion, respectively. Also, the composition x = 17.5 at which a second maximum is seen in the thermal diffusivity has been identified to be the chemical threshold (CT) of the As20Te80−xGax glassy system, as at CT, the glass is configurationally closest to the crystalline state and the scattering of the diffusing thermal waves is minimal for the chemically ordered phase. |
| |
Keywords: | 65.60.+a 66.30.Xj 78.20.Nv |
本文献已被 ScienceDirect 等数据库收录! |
|