Study of solid-phase reaction of RbNO3 with V2O5 |
| |
Authors: | Ľ Žúrková V Suchá K Gáplovská |
| |
Institution: | (1) Department of Inorganic Chemistry, Faculty of Natural Sciences, Comensky University, 81631 Bratislava, Czechoslovakia |
| |
Abstract: | Using DTA, TG and DTG methods, the reaction between RbNO3 and V2O5 in the molar ratio 65 in air atmosphere was studied. The reaction proceeds stepwise. In individual steps of the reaction the formation of RbV3O8, RbVO3 and Rb3V5O14 was observed. Rubidium pentavanadate is thermally unstable. At 1000°, RbVO3 and Rb2V4O11 were identified as products of its thermal decomposition. Rubidium tetravanadate was also prepared by the isothermal reaction of RbNO3 with V2O5 in the molar ratio 11.
Zusammenfassung Unter Anwendung der DTA-, TG- und DTG-Methoden wurde die Reaktion RbNO3-V2O6 bei dem Molverhältnis von 65 in Luft untersucht. Die Reaktion verläuft stufenweise. Bei den einzelnen Stufen der Reaktion wurde die Bildung von RbV3O8, RbVO3 und Rb3V5O14 beobachtet. Rubidiumpentavanadat ist thermisch instabil. Bei 1000° wurden RbVO3 und Rb2V4O11 als Produkte seiner thermischen Zersetzung beobachtet. Rubidiumtetravanadat wurde auch durch die isotherme Reaktion von RbNO3-V2O5 bei dem Molverhältnis von 11 hergestellt.
Résumé On a étudié par ATD, TG et TGD dans l'air, la réaction RbNO3-V2O5 (rapport molaire 65). La réaction s'effectue par étapes, avec formation de RbV3O8, RbVO3 et Rb3V5O14. Le pentavanadate de rubidium est thermiquement instable. A 1000°, RbVO3 et Rb2V4O11 ont été identifiés comme produits de la décomposition thermique. Le tétravanadate de rubidium a également été préparé par voie isotherme en faisant réagir RbNO3-V2O5 (rapport molaire 11).
, , RbNO3-V2O5 6 5. . RbV3O8, RbVO3 Rb3V5O14. 1000° RbVO3 Rb2V4O11, . RbVO3-V2O5 11. |
| |