Evidence for ordered regions in poly(n-butyl)methacrylate from light-scattering studies

From light-scattering studies on polybutylmethacrylate, a polymeric glass, the variation of the velocity and attenuation of thermally excited hypersonic phonons with temperature has been measured. Measurement of the temperature dependence of the ratio of the intensity of the Rayleigh line to the Brillouin lines is interpreted as due to a configurational rearrangement within the glass above the glass transition temperature, T_g . Only light scattered from longitudinal phonons was observed. The distinct change in the temperature dependence of the velocity, attenuation and intensity ratio identified the glass transition.

For samples annealed well above T_g, T_g was found to be about 0°C from the light-scattering studies, 12°C from differential scanning calorimetry (DSC), and 20°C from refractive index measurements. For an unannealed sample the behaviour of the above parameters with temperature was found to be different. T_g for the unannealed sample was 14°C from light-scattering, 18°C from DSC and 20°C from index of refraction measurements.