Composite hollow fiber membranes for CO2 capture

Composite hollow fibers membranes were prepared by coating poly(phenylene oxide) (PPO) and polysulfone (PSf) hollow fibers with high molecular polyvinylamine (PVAm). Two procedures of coating hollow fibers outside and respective inside were investigated with respect to intrinsic PVAm solution properties and hollow fibers geometry and material.The influence of operating mode (sweep or vacuum) on the performances of membranes was investigated. Vacuum operating mode gave better results than using sweep because part of the sweep gas permeated into feed and induced an extra resistance to the most permeable gas the CO₂. The composite PVAm/PSf HF membranes having a 0.7–1.5 μm PVAm selective layer, showed CO₂/N₂ selectivity between 100 and 230. The selectivity was attributed to the CO₂ facilitated transport imposed by PVAm selective layer. The CO₂ permeance changed from 0.006 to 0.022 m³(STP)/(m² bar h) in direct correlation with CO₂ permeance and separation mechanism of the individual porous supports used for membrane fabrication. The multilayer PVAm/PPO membrane using as support PPO hollow fibers with a 40 nm PPO dense skin layer, surprisingly presented an increase in selectivity with the increase in CO₂ partial pressure. This trend was opposite to the facilitated transport characteristic behaviour of PVAm/porous PSf. This indicated that PVAm/PPO membrane represents a new membrane, with new properties and a hybrid mechanism, extremely stable at high pressure ratios. The CO₂/N₂ selectivity ranged between 20 and 500 and the CO₂ permeance from 0.11 to 2.3 m³(STP)/(m² bar h) depending on the operating conditions.For both PVAm/PSf and PVAm/PPO membranes, the CO₂ permeance was similar with the CO₂ permeance of uncoated hollow fiber supports, confirming that the CO₂ diffusion rate limiting step resides in the properties of the relatively thick support, not at the level of 1.2 μm thin and water swollen PVAm selective layer. A dynamic transfer of the CO₂ diffusion rate limiting step between PVAm top layer and PPO support was observed by changing the feed relative humidity (RH%). The CO₂ diffusion rate was controlled by the PPO support when using humid feed. At low feed humidity the 1.2 μm PVAm top layer becomes the CO₂ diffusion rate limiting step.